Studies of the hardness for the sintered tantalum boride (TaB) at high temperature and high pressure
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用国产DS6×800T铰链式六面顶压机技术,对过渡金属TaB粉末进行了高温高压烧结,并采用金刚石菱形压痕法对TaB维氏硬度进行了测量。在加载负荷为29.4 N时,烧结压力为4 GPa,烧结温度分别为900和1100 ℃时,测试得到TaB陶瓷的硬度分别为7.7±0.4和 10.5±0.7 GPa。说明在同一压力条件下,温度越高致密性越好,通过阿基米德法,计算得到了TaB的相对密度为13.5 g/cm3。

    Abstract:

    Tantalum boride has been sintered under high temperature and high pressure (HTHP) conditions by using a DS6×8 MN cubic press device, and the Vickers hardness of TaB has been measured by using a diamond indentation method. Under the applied load of 29.4 N, our test gave the Vickers hardness of TaB are 7.7±0.4 and 10.5±0.7 GPa, at 4 GPa and the temperatures of 900 and 1100 ℃, respectively. Our result shows that the density becomes better with the increasing temperature under the same pressure. By using the Archimedes method, we calculated the relative density of 13.5 g/cm3 for TaB.

    参考文献
    相似文献
    引证文献
引用本文

引用本文格式: 陈海花,梁浩,谢名财,刘凌霄,郑曙东. 硼化钽(TaB)高温高压烧结体硬度的研究[J]. 四川大学学报: 自然科学版, 2017, 54: 835.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2017-04-09
  • 最后修改日期:2017-05-01
  • 录用日期:2017-05-18
  • 在线发布日期: 2017-07-03
  • 出版日期: