Preparation and Characterization of V- doped Titanium Dioxide Films used for Dye-sensitized Solar Cell
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为获得高性能电池用二氧化钛薄膜,采用射频磁控溅射法在靶材中掺入V2O5制备了TiO2薄膜,使用分光光度计和电化学工作站研究了溅射时间、退火温度和掺钒量等对TiO2薄膜光学性能和电学性能的影响。研究表明溅射时间对薄膜紫外光区的透射率影响较大,在小于400nm区域内,3h溅射薄膜的透射率已经降至60%以下;对薄膜可见光区的透射率影响较小,此区域内薄膜的平均透射率达80%以上。退火温度对薄膜的亲水性能和光催化性能有一定的影响,经400℃退火的薄膜具有很好的光催化性能和超亲水性。掺杂V2O5使薄膜的吸收峰红移和禁带宽度变窄,当掺杂量为0.5%时,TiO2薄膜红移量最大、禁带宽度变为2.88eV。随后将制备的掺钒二氧化钛薄膜制备成染料敏化太阳能电池(DSSC),结果表明掺V2O5 0.5%的二氧化钛薄膜的光响应范围增大,所制备电池的开路电压和短路电流都高于未掺杂电池,特别是短路电流从24.82μA增大到了88.15μA,提高了电池的综合性能。

    Abstract:

    In order to obtain high-performance batteries with titanium dioxide films by RF magnetron sputtering, doped(V2O5) TiO2 films were prepared. The main factors affecting the time,the pressure ratio of argon and oxygen, and annealing temperature. The effects such as mass of doping (V2O5) and annealing temperature on film properties.722 spectrophotometer using the optical properties of the study by the degradation of methylene blue and drop contact angle method on the catalytic properties of thin films and hydrophilic properties were studied. The results showed that Doped (V2O5) red shift the absorption peak of the film and the band gap narrowing, of which 0.5% V2O5 doped TiO2 thin film of the red shifts of the largest band gap becomes 2.88eV; 400℃ annealed films with good photocatalytic properties and ultra-hydrophilic.The prepared thin films of titanium dioxide as DSSC cells of sputtering time, the doping effect on battery performance. it shows that Doped with 0.5% V2O5 thin film battery open circuit voltage and short circuit current is higher than the undoped cell, in particular, short-circuit current increases from 24.82A to 88.15A.

    参考文献
    相似文献
    引证文献
引用本文

引用本文格式: 赖奇,廖先杰,张树立,李俊翰,吴恩辉,钟璨宇. DSSC用钒掺杂二氧化钛薄膜的制备及性能表征[J]. 四川大学学报: 自然科学版, 2017, 54: 1289.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2017-03-16
  • 最后修改日期:2017-04-08
  • 录用日期:2017-05-03
  • 在线发布日期: 2017-11-08
  • 出版日期: