Ultrasonic Dispersion method Preparation and Photocatalytic Performance of WS2/TiO2 Composite Photocatalyst
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文采用超声分散方法制备WS2/TiO2复合物,在光照条件下,对罗丹明B的降解效果进行了一系列研究。在确定WS2与TiO2的混合比例后,同时又对WS2/TiO2煅烧温度、煅烧时间、催化剂的用量、光照时间、光照功率、染料浓度等影响因素分别进行了讨论。实验结果表明,催化剂的量为1.00 g/L、染料的初始浓度为10.00 mg/L,WS2/TiO2(1:11)、焙烧温度为350 °C、焙烧时间为90 min时,对罗丹明B染料的降解效果最佳。

    Abstract:

    WS2/TiO2 composite was prepared by using the ultrasonic dispersion method, and the effect of degradation of Rhodamine B was studied under irradiation conditions. The influence factors on the degradation efficiency, such as calcination temperature and time of WS2/TiO2 , the amount of catalyst, illumination time, irradiation intensity, and initial concentration of Rhodamine B were discussed, respectively. The experimental results revealed that the best degradation efficiency of Rhodamine B based on the amount of catalyst was 1.00 g/L, the initial concentration was 10.00 mg/L, the m(WS2):m(TiO2) was 1:11, and the calcination temperature and time were 350 °C and 90 min, respectively.

    参考文献
    相似文献
    引证文献
引用本文

引用本文格式: 杜意恩,白杨,刘毓芳,蔡雪梅,郭彦青. 超声分散法制备WS2/TiO2复合光催化剂及其光催化性能[J]. 四川大学学报: 自然科学版, 2017, 54: 829.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-04-08
  • 最后修改日期:2016-05-08
  • 录用日期:2016-05-11
  • 在线发布日期: 2017-07-03
  • 出版日期: